Flashforge DLP Resin 0.5KG Bottle for DLP 3D Printers

• Ideal for rapid prototyping and production.

FH1100

FH1100 shows a great modeling effect on both suspended structure and flowing structure, the final printing result is smooth and neat with refined details. Designed for high precision pattern production, Flashforge FH1100 is ideal for rapid prototyping and production.

Produced under strict manufacturing and quality control standards, Flashforge FH1100 has high stability, with low shrinkage and low failure rates.

Material Properties:

Density: 1.09-1.12g／ml

Viscosity: 400-550cps

Tensile Strength: 42 MPa

Elongation at Break: 17%

Shore Hardness: 85 D

Exposure Ec: 6 mj/cm2

Penetration Depth: 8 mil (0.2mm)

FH1200

Flashforge's castable resin has many advantages such as non-toxic, low odor, high detail, and rapid curing. The printed models show good strength, toughness, flexibility, and high impact resistance. The resin burns out cleanly with no ash or residue.

Material Properties:

Tensile Strength: 10 MPa

Elongation at Break: 8.5%

Flexural Strength: 27 MPa

Flexural Modulus: 920 MPa

Shore Hardness: 70D

Volumetric Shrinkage: 5.58%-6.02%

Applications: Jewelry

FHD1200

Main Properties:

Tensile Strength: 35-42MPa

Elongation at Break: 10~20%

Flexural Strength: 62-70Mpa

Density: 1.038g／ml

Shore Hardness: 84D

Volume Contraction Rate: 2.5%

Viscosity: 50±20 mPa.s

FHD1300

Main Properties:

Tensile Strength: 60.5MPa

Elongation at Break: 0.04

Density: 1.118g／ml

Shore Hardness: 81D

Volume Contraction Rate: 6.74%

Viscosity: 120cps

FHD1400

Main Properties:

Tensile Strength: 45MPa

Elongation at Break: 15%

Flexural Strength: 53MPa

Flexural Modulus: 1200MPa

Density: 1.09-1.12g／ml

Shore Hardness: 82D

Volume Contraction Rate: 3-5%

Viscosity: 350-500cps

Size: Big Package (37.5*15.5*23.5cm)／Small Package (14*7*21.5cm)

Specification: 500ml*10／500ml*2